Title 簡易的な金属間化合物創製プロセスの提案とその実現  
Kana カンイテキナ キンゾクカン カゴウブツ ソウセイ プロセス ノ テイアン ト ソノ ジツゲン  
Romanization Kanitekina kinzokukan kagobutsu sosei purosesu no teian to sono jitsugen  
Other Title
Title Proposal of metallic-compound creating process  
Kana  
Romanization  
Creator
Name 小茂鳥, 潤  
Kana コモトリ, ジュン  
Romanization Komotori, Jun  
Affiliation 慶應義塾大学・理工学部・教授  
Affiliation (Translated)  
Role Research team head  
Link 科研費研究者番号 : 30225586

Name 村井, 一恵  
Kana ムライ, カズエ  
Romanization Murai, Kazue  
Affiliation 慶應義塾大学・理工学部・助教  
Affiliation (Translated)  
Role Research team member  
Link 科研費研究者番号 : 70645944
Edition
 
Place
 
Publisher
Name  
Kana  
Romanization  
Date
Issued (from:yyyy) 2016  
Issued (to:yyyy)  
Created (yyyy-mm-dd)  
Updated (yyyy-mm-dd)  
Captured (yyyy-mm-dd)  
Physical description
1 pdf  
Source Title
Name 科学研究費補助金研究成果報告書  
Name (Translated)  
Volume  
Issue  
Year 2015  
Month  
Start page  
End page  
ISSN
 
ISBN
 
DOI
URI
JaLCDOI
NII Article ID
 
Ichushi ID
 
Other ID
 
Doctoral dissertation
Dissertation Number  
Date of granted  
Degree name  
Degree grantor  
Abstract
雰囲気制御高周波誘導加熱微粒子ピーニングシステムを用いて, 鋼表面にNi-Al金属間化合物層の創成を試みた。その結果, NiとAl粒子を1 : 4の割合で混練した粒子でAIH-FPPを施すと, Ni-Al金属間化合物層が形成された。これは, 投射粒子に含まれるAlがフラックスとして作用することにより局所的にNiとFeの融点が低下すること, また, NiとAlの燃焼合成反応により, 局所的に温度が上昇したためである。さらに, 高温連続酸化試験の結果, 処理した部位は優れた耐酸化性を持つことがわかった。これは, Ni-Al金属間化合物層が高温酸化雰囲気中でAl2O3を連続的に生成しそれが保護被膜となるためである。
To form a Ni-Al intermetallic compound layer on a carbon steel surface, AIH-FPP was carried out at 900℃ in argon atmosphere with a Ni and Al particle milled by means of planetary ball mills. The treated surface was analyzed using SEM, EDX and an XRD. Oxidation test was carried out at 900℃ for 100 hours. Results showed that the Ni-Al intermetallic compound layer with a thickness of 200 μm was formed in the case of the specimen treated by the aluminum rich shot particles; the ratio of Ni to Al was 1 to 4 at.%. This was because (i) melted Al particles reduced the melting point of Ni particles and Fe substrate, and (ii) partially melted area promoted a combustion synthesis reaction between Ni and Al, resulting in forming the Ni-Al intermetallic compound layer. The AIH-FPP treated surface showed a higher oxidation resistance than that of the un-treated specimen. This was because Al2O3 continually created from the Ni-Al intermetallic compound layer protected the steel substrate.
 
Table of contents

 
Keyword
微粒子ピーニング  

高周波誘導加熱  

表面改質  

金属間化合物  
NDC
 
Note
研究種目 : 挑戦的萌芽研究
研究期間 : 2014~2015
課題番号 : 26630013
研究分野 : 材料工学
 
Language
日本語  

英語  
Type of resource
text  
Genre
Research Paper  
Text version
publisher  
Related DOI
Access conditions

 
Last modified date
Dec 27, 2016 11:19:08  
Creation date
Dec 27, 2016 11:19:08  
Registerd by
mediacenter
 
History
 
Index
/ Public / Grants-in-Aid for Scientific Research / Fiscal year 2015 / Japan Society for the Promotion of Science
 
Related to
 

Ranking

most accessed items
1st 新自由主義に抗す... (427) 1st
2nd 斎藤隆夫の「粛軍... (340)
3rd 慶應義塾図書館史... (271)
4th 認知文法から考え... (265)
5th M&Aにおける... (263)

most downloaded items
1st <<Qu'... (1470) 1st
2nd 新参ファンと古参... (437)
3rd 731部隊と細菌戦 ... (314)
4th 日本における美容... (268)
5th 新自由主義に抗す... (267)

LINK

慶應義塾ホームページへ
慶應義塾大学メディアセンターデジタルコレクション
慶應義塾大学メディアセンター本部
慶應義塾研究者情報データベース